ASN Wikibase Occurrence # 314416
This information is added by users of ASN. Neither ASN nor the Flight Safety Foundation are responsible for the completeness or correctness of this information.
If you feel this information is incomplete or incorrect, you can submit corrected information.
| Date: | Monday 12 March 2012 |
| Time: | 19:55 LT |
| Type: |  Beechcraft 1900D |
| Owner/operator: | Great Lakes Aviation |
| Registration: | N178YV |
| MSN: | UE-178 |
| Total airframe hrs: | 33249 hours |
| Engine model: | P&W PT6A SER |
| Fatalities: | Fatalities: 0 / Occupants: |
| Aircraft damage: | Minor |
| Category: | Serious incident |
| Location: | Hays, Kansas -
 United States of America
|
| Phase: | Standing |
| Nature: | Unknown |
| Departure airport: | Denver International Airport, CO (DEN/KDEN) |
| Hays Municipal Airport, KS (HYS/KHYS) | |
| Investigating agency: | NTSB |
| Confidence Rating: |  Accident investigation report completed and information captured |
During a post flight inspection the pilot discovered a hydraulic leak on the nose landing gear that was emanating from a crack in the nose landing gear end cap. The end cap was examined and found to have failed in fatigue that initiated from multiple origins at an internal diameter. The fatigue had propagated significantly into the wall thickness of the end cap and through the thickness at one location. The striation count revealed that the fatigue crack had initiated and been growing in the end cap for at least 22,563 cycles. The end cap had been inspected using an ultrasonic method recommended by the manufacturer 3 cycles prior to the incident. The crack was present at the time of the inspection which indicated that the inspection method was ineffective in detecting the crack. The timing of the end cap inspection was in compliance with the manufacturer's recommendation. The crack was also present at the time of the last overhaul. Examination of the microstructure of the material revealed that the longitudinal grain direction was oriented parallel to the shuttle valve bore in the end cap. Resistance to fatigue can be improved by aligning the principle tension stresses in the end cap with the longitudinal grain direction. It is probable that the manufacturer had determined that the grain direction was a contributing factor to fatigue failure in the end cap and revised the end cap drawing to require a grain direction along the longitudinal axis of the end cap in February 2010. No engineering data to support the drawing revision was made available.
Probable Cause: A failure of the nose landing gear end cap due to fatigue. Contributing to the failure were the ineffective inspection and the unknown effect of grain direction on fatigue life.
Accident investigation:
 |
|
Sources:
NTSB ENG12IA024
Location
Revision history:
| Date/time | Contributor | Updates |
|---|---|---|
| 02-Jun-2023 17:14 | ASN Update Bot | Added |
Corrections or additions? ... Edit this accident description
The Aviation Safety Network is an exclusive service provided by:
Quick Links:
| ASN Home | Send Correction / Feedback |
| FSF Home | Disclaimer | Copyright |
| Contact Us | Privacy Policy |
| Press / Media |
CONNECT WITH US:
©2024 Flight Safety Foundation